Raising carbon content in the base metal makes the welded joint more prone to cracking because it tends to form harder, more brittle microstructures in the heat-affected zone when the weld cools. That brittleness increases the risk of cracks developing in the weld metal or adjacent areas, especially with the rapid cooling that can occur in GMAW.

To counter this in practice, you preheat the workpiece to raise the starting temperature and slow the cooling rate, which helps keep the microstructure from becoming too brittle. You also choose a filler metal whose carbon content and alloying elements are compatible with the base metal, so the weld metal remains tough rather than overly hard. Finally, you carefully control the heat input—neither too high nor too low—so the weld penetrates properly without promoting brittle microstructures from rapid cooling. Together, these steps reduce cracking risk when working with higher-carbon steels.